Volume 19 Issue 1
Jul.  2017
Turn off MathJax
Article Contents

FU Shen-yuan, LU Jian-quan, YU Hong-wei, HUAI Min. Synthesis of copolymer acrylates-vinyl emulsion and wood cold pressing adhesive[J]. Journal of Zhejiang A&F University, 2002, 19(1): 12-16.
Citation: FU Shen-yuan, LU Jian-quan, YU Hong-wei, HUAI Min. Synthesis of copolymer acrylates-vinyl emulsion and wood cold pressing adhesive[J]. Journal of Zhejiang A&F University, 2002, 19(1): 12-16.

Synthesis of copolymer acrylates-vinyl emulsion and wood cold pressing adhesive

Funds:

国家星火计划项目(2001EA700003)

  • Received Date: 2001-11-06
  • Rev Recd Date: 2001-12-24
  • Publish Date: 2002-03-20
通讯作者: 陈斌, bchen63@163.com
  • 1. 

    沈阳化工大学材料科学与工程学院 沈阳 110142

  1. 本站搜索
  2. 百度学术搜索
  3. 万方数据库搜索
  4. CNKI搜索

Article views(1424) PDF downloads(148) Cited by()

Related
Proportional views

Synthesis of copolymer acrylates-vinyl emulsion and wood cold pressing adhesive

Funds:

国家星火计划项目(2001EA700003)

Abstract: By synthesis process of copolymer acrylates-vinyl emulsion adhesive , the effects of influencing of the emulsion adhesive quality were analyzed and investigated .Both optimun synthesis process (polymerization temperature is 85 ℃, ploymerization time 4 h , initiator 0.4 % ~ 0.6 %) and wood cold pressing adhesive conditions were selected .It was proved that it was easy of manipulating for the bonding , was good at forming film for the emulsion , and could be used every where .The bonding strength could meet requirements speeified in standard GB/T17657-1999 (Ⅰ)plywood (bonding strength 0.965 MPa) for cold pressing adhesive of the emulsion .

FU Shen-yuan, LU Jian-quan, YU Hong-wei, HUAI Min. Synthesis of copolymer acrylates-vinyl emulsion and wood cold pressing adhesive[J]. Journal of Zhejiang A&F University, 2002, 19(1): 12-16.
Citation: FU Shen-yuan, LU Jian-quan, YU Hong-wei, HUAI Min. Synthesis of copolymer acrylates-vinyl emulsion and wood cold pressing adhesive[J]. Journal of Zhejiang A&F University, 2002, 19(1): 12-16.

Catalog

    /

    DownLoad:  Full-Size Img  PowerPoint
    Return
    Return