Hot pressing technology of fast-curing for cement particle board

YE Liang-ming; JIANG Zhi-hong; BAO Bing-fu; YU Xue-jun; YU You-ming

PDF
Cite
Share

facebook

twitter

google

linkedin

Volume 19 Issue 2

Jul. 2017

Turn off MathJax

Article Contents

Article Navigation > Journal of Zhejiang A&F University > 2002 > 19(2): 118-121

YE Liang-ming, JIANG Zhi-hong, BAO Bing-fu, YU Xue-jun, YU You-ming. Hot pressing technology of fast-curing for cement particle board[J]. Journal of Zhejiang A&F University, 2002, 19(2): 118-121.

Citation:

YE Liang-ming, JIANG Zhi-hong, BAO Bing-fu, YU Xue-jun, YU You-ming. Hot pressing technology of fast-curing for cement particle board[J]. Journal of Zhejiang A&F University, 2002, 19(2): 118-121.

Hot pressing technology of fast-curing for cement particle board

1.
Faculty of Engineering , Zhejiang Forestry College , Lin'an 311300 , Zhejiang , China

Publish Date: 2002-06-20

Abstract

How hot pressing temperature , hot pressing time and the additive level of sodium silicate acted the properties of cement particle board were made by fast-curing hot pressing , using ternary quadratic orthogonal rotation design when cement/wood was 2.6 , water/cement 0.6 , hot pressing pressure 2.8 MPa , the designed density 1.2 gcm -3 , and the thickness 9 mm .The results showed that hot pressing temperature notably acted modulus of rupture (MOR), internal bowding (IB), thichness spread (TS), density , and the relationship was parabola , but it did not act modulus of elasti city (MOE);that hot pressing time notably acted MOE , IB , TS and density , and the relationship was linear ;that the additive level of sodium silicate notably acted MOR , IB and density , and the relationshp was parabola ;that the optimum hot pressing technology was that temperature was 100 ℃, time 12 min , the additive level of sodium silicate 100 gkg-1 .
- cement particle board,
- fast curing,
- hot pressing technology,
- orthogonal rotation design,
- Cunninghamia lanoeolata

Relative Article

[1]	YU Le, Lü Jianxiong, LI Xianjun, XU Kang, WU Yiqiang, JIANG Jiali. Comparison of X-ray scanning and slice methods for moisture distribution measurements when drying Cunninghamia lanceolata plantation wood . Journal of Zhejiang A&F University, 2013, 30(4): 543-547. doi: 10.11833/j.issn.2095-0756.2013.04.013
[2]	ZHU Xiang-hui, WANG Chuan-jia, WANG Ren-dong, WENG Yong-fa, MA Fei-jie, GUO Lu, FANG Huai-yuan, ZHU Tang-jun. Study on the methodology for monitoring Chinese fir carbon sink of CDM-afforestation and reforestation(AR) project . Journal of Zhejiang A&F University, 2008, 25(3): 336-341.
[3]	LIANG Hong-wen, HUANG Heng-chuan, HUANG Cheng-biao, HUANG Hai-zhong, LIANG Xin, MENG Yue-huan. Wood physical-mechanical properties of Taiwania flousiana compared to Cunninghamia lanceolata for plantation development . Journal of Zhejiang A&F University, 2008, 25(2): 137-142.
[4]	MA Ling-fei, JI Wei-bing. Simple method for producing strand used in laboratory . Journal of Zhejiang A&F University, 2007, 24(1): 96-99.
[5]	JIANG Zong-kai. Dynamics of nitrogen and phosphorus standing stocks in fine roots of Fokienia hodginsii and Cunninghamia lanceolata plantations . Journal of Zhejiang A&F University, 2007, 24(1): 33-38.
[6]	FUShun-hua, DONG Ru-xiang, WULong-gao, FENG Jian-min, LIUWei-hong, HUA Chao-hui, SUNHong-you. Correlations in progeny trials of Cunninghamia lanceolata . Journal of Zhejiang A&F University, 2007, 24(3): 272-278.
[7]	BAO Bin-fu, SHA Cun-long, YU Wen-jun, JIANG Zhi-hong, YU You-ming, YU Xue-jun. Effects of final treatment techniques on the properties of fast curing cement particle board . Journal of Zhejiang A&F University, 2006, 23(3): 237-241.
[8]	BAO Bin-fu, YU Wen-jun, JIANG Zhi-hong, YU You-ming. Effect of hot-pressing temperature and natural curing time on properties of fast-curing cement particle board . Journal of Zhejiang A&F University, 2006, 23(2): 129-134.
[9]	DU Chun-gui, LIU Zhi-kun, ZHANG Qi-sheng, ZHANG Hong, LOU Yong-sheng. Overlaying technology of paper impregnated thermosetting resins of Chinese fir orient laminated strand lumber . Journal of Zhejiang A&F University, 2004, 21(2): 134-137.
[10]	JIN Yong-ming, QIAN Jun, LOU Jian-qiang, YU You-ming, YE Liang-ming. Study on manufacturing joiner core by PSL method . Journal of Zhejiang A&F University, 2003, 20(1): 5-7.
[11]	JIN Yong-ming, BAO Bing-fu, CHEN Qing-hu, YU Xue-jun, YU You-ming, YE Liang-ming. Effects of assembly time and cement/wood ratio on properties of . Journal of Zhejiang A&F University, 2003, 20(3): 232-235.
[12]	JIN Yong-ming, YU You-ming, YE Liang-ming. Effects of wood shaving shapes on the properties of quick-curing cement particle board . Journal of Zhejiang A&F University, 2003, 20(3): 236-239.
[13]	SHEN Zhe-hong, FANG Qun, QIAN Jun. Technology of bond joint Chinese fir-core blockboard . Journal of Zhejiang A&F University, 2002, 19(2): 208-210.
[14]	YE Liang-ming, JIN Yong-ming, FU Shen-Yuan, LI Yan-jun. Selection of chemical additives with function of fast curing for cement particle board . Journal of Zhejiang A&F University, 2002, 19(1): 5-8.
[15]	WU Jia-sheng, YING Ye-qing, TONG Yong-bo, DING Ling, ZHOU Jian-guang. Seedling growing on elite families of Chinese fir . Journal of Zhejiang A&F University, 2000, 17(1): 9-13.
[16]	XU Feng-lan, WEI Tan, LIU Ai-qing. Studies on physical characters of soil in mixed forest of Chinese fir and paulownia . Journal of Zhejiang A&F University, 2000, 17(3): 285-288.
[17]	Cheng Shuwnn, Wang Gaiping, Ding Guohua, Ye Jingzhong. Nitrogen Nutrition in Sprouting Buds from Chinese Fir Stumps . Journal of Zhejiang A&F University, 1995, 12(2): 133-138.
[18]	Wu Zuying, Sun Hongyou, Jiang Liuqi, Tang Mingrong, Ni Rongxin.. Selection of Soybean Varieties Suitable for Interplant in the Young Growth of Chinese Fir. . Journal of Zhejiang A&F University, 1995, 12(1): 13-23.
[19]	He Fuji, Yu Xiangyu, Li Ping.. Preliminary Inheritance Analysis to Male Sterility of Chinese Fir. . Journal of Zhejiang A&F University, 1995, 12(2): 219-220.
[20]	Guab Kanglin, Yan Yilun, Zhen Gang. Developmental Physiology of Cunninghamia lanceolata . Journal of Zhejiang A&F University, 1994, 11(2): 105-115.

References
Proportional views

通讯作者: 陈斌, bchen63@163.com

1.
沈阳化工大学材料科学与工程学院沈阳 110142

Get Citation

PDF

XML

Article views(1325) PDF downloads(215) Cited by()

Proportional views

Hot pressing technology of fast-curing for cement particle board

1. Faculty of Engineering , Zhejiang Forestry College , Lin'an 311300 , Zhejiang , China

Publish Date: 2002-06-20

Key words:

Abstract: How hot pressing temperature , hot pressing time and the additive level of sodium silicate acted the properties of cement particle board were made by fast-curing hot pressing , using ternary quadratic orthogonal rotation design when cement/wood was 2.6 , water/cement 0.6 , hot pressing pressure 2.8 MPa , the designed density 1.2 gcm -3 , and the thickness 9 mm .The results showed that hot pressing temperature notably acted modulus of rupture (MOR), internal bowding (IB), thichness spread (TS), density , and the relationship was parabola , but it did not act modulus of elasti city (MOE);that hot pressing time notably acted MOE , IB , TS and density , and the relationship was linear ;that the additive level of sodium silicate notably acted MOR , IB and density , and the relationshp was parabola ;that the optimum hot pressing technology was that temperature was 100 ℃, time 12 min , the additive level of sodium silicate 100 gkg-1 .

YE Liang-ming, JIANG Zhi-hong, BAO Bing-fu, YU Xue-jun, YU You-ming. Hot pressing technology of fast-curing for cement particle board[J]. Journal of Zhejiang A&F University, 2002, 19(2): 118-121.

Citation:

YE Liang-ming, JIANG Zhi-hong, BAO Bing-fu, YU Xue-jun, YU You-ming. Hot pressing technology of fast-curing for cement particle board[J]. Journal of Zhejiang A&F University, 2002, 19(2): 118-121.

HTML

DownLoad: Full-Size Img PowerPoint

Return

Hot pressing technology of fast-curing for cement particle board

Abstract

References

Proportional views

通讯作者: 陈斌, bchen63@163.com

Related

Proportional views

Hot pressing technology of fast-curing for cement particle board

1. Faculty of Engineering , Zhejiang Forestry College , Lin'an 311300 , Zhejiang , China

HTML

Catalog

Hot pressing technology of fast-curing for cement particle board

Abstract

Relative Article

References

Proportional views

通讯作者: 陈斌, bchen63@163.com

Related

Proportional views

Hot pressing technology of fast-curing for cement particle board

1. Faculty of Engineering , Zhejiang Forestry College , Lin'an 311300 , Zhejiang , China

HTML

Catalog

Export File

Citation

Format

Content